MATERIALS AND SURFACE Coatings

FASTENER COATINGS & SURFACE TREATMENTSTOP COATSBASECOATSASTMASTM A153/A153M (HDG)ASTM F2329/F2329M (HDG)ASTM F2833 (ZN AL+)ASTM B595 (MECH ZN)ZINC FLAKEDACROMETDACROMET 320DACROMET 500ISOISO 4042 (ZN/ZNNI/CD+)ISO 15726 (ZNNI)SEALANTSMOLYKOTEASTM F1136/F1136M ZNAL+)GEOMETGEOMET 321GEOMET 500GEOMET 720ASTM F3019/3019M ZN FLAKE)XYLARXYLAR 2PTFETEFLONXYLANXYLAN 1070XYLAN 1424ARMORCOTE POLYOLEFINDELTA TONE/SEALHSFG FASTENERSSHERARDIZEDXYLAN ZINC RICHTAKECOATMAGNICARDXYLAN 1014ASTMASTM 8766 (CD+)ASTM B840 (ZNCO+)ZINC NICKELSERMAGARD 1105SERMAGARD 1280ELECTROLESS NICKELCADMIUMTINGOLDSILVERSERMAGARDISO 10683 (ZN FLAKE)ASTM 8841 (ZNNI+)ASTM 8994 (CONI+)ASTM F1137 (PHOSPHATE)ASTM F1428 (AL+)ASTM F1941/M (ZN/CD/NI/CO/FE)XYLAR 101

surface finishes and plating

1No finishNO FINISH

2

Anodized (Dk. Gray)ANODIZE-MIL-A-8625F, Type II – Class 2 – (Sulphuric) Hot Water Seal. (Dk. Gray)
3aAnodized (Clear)ANODIZE-MIL-A 8625F, Type II – Class I – (Sulphuric) Hot water Seal. (Clear)
3bAnodized (Blue)ANODIZE-MIL-A-8625F, Type II – Class 2 – (Sulphuric) Hot Water Seal. (Blue)
3cAnodized (Red)ANODIZE-MIL-A-8625F, Type II – Class 2 – (Sulphuric) Hot water seal (Red)
4aAnodized (Yellow Green)ANODIZE-MIL-A-8625F, Type II – Class 2 – (Sulphuric) Dichromate Seal (Yellow Green)
4bAnodized (Dichromate)ANODIZE-MIL-A-8625F- Type II (Sulphuric) Dichromate Seal (Red)
4cAnodized (Dyed Gold)ANODIZE – MIL-A-8625F-Type II Class 2 (Dyed Gold)

5

Anodized (Black)ANODIZE-MIL-A-8625F, Type II – Class 2 Hot water Seal (Black)

6a

Cadmium Plate ClearCADMIUM PLATE QQ-P-416-F-Type I-Class 2-Clear Chromate
6bCadmium Plate ColorCADMIUM PLATE, QQ-P-416-F-Type II- Class 2 Color Chromate Finish”
7Cadmium Commercial Plate,CADMIUM PLATE COMMERCIAL – Type I, Class 3
8Cadmium Color Chromate PlateCADMIUM PLATE QQ-P-416-F-Type II – Class 3 – Color Chromate Finish

9a

Nickel Plate, Grade GNICKEL PLATE – QQN-290-A-Class 1, Grade G, (thickness – .0002- SB) (single layer coating fully bright)
9bNickel Plate, Grade FNICKEL PLATE – QQN290-A Class 1, Grade F (Thickness -.0004-SB) (single layer coating fully bright)

10

Silver PlateSILVER PLATE – QQ-S-365-D, Type II – Grade B (Thickness -.0003)

11a

Black oxide, Class 4BLACK OXIDE – MIL-C-13924-C-AMEND #1 Class 4. For 300 series corrosion resistance steel alloys only.
11bBlack oxide, Class 1BLACK OXIDE – MIL-C-13924-C-AMEND #1 – Class 1 (for plain carbon and low alloy steels)

12a

Passivate, Type IPASSIVATE – MIL-F-14072-C (ER) AMEND #1 – Type I. (Finish #E300 – Passivate per ASTM-A-380-96)
12bPassivate, Type IIPASSIVATE QQ-P-35C, Type II.”

13

Alodine 1200ALODINE 1200
14Gold FlashGOLD FLASH, (Thickness -.00003 to .00005.)
15Gold Flash over NickelGOLD FLASH over Nickel Flash, (Thickness – .00003 to .00005)
16Gold PlateGOLD PLATE MIL-G-45204-C-AMEND #1, Type 11 – Grade C – Class-2 (Thickness .0001 0 minimum)

17

Tin Plate IITIN PLATE (Hot dipped) MIL-T-10727-C, Type II
18aTin Plate IITIN PLATE (Electro Deposit) MIL-T-10727-C, Type I
18bTin Plate I (solderable)TIN PLATE (Electro Deposit) MIL-T-10727-C, Type I plus solderability ASTM B 545-92, Class-C”

19

Bright Dip BrassBRIGHT DIP (Brass Finish)

20a

IRIDITE (Clear)IRIDITE – MIL-C-5541-E-Class 3 (clear)
20bIRIDITE (Gold)IRIDITE – MIL-C-5541-E-Class la (Gold)
21Gold Flash over SilverGOLD FLASH 0.000015 thick over Silver-Plate (0.0003 thickness)

22

Chomium BrightCHROMIUM PLATING – QQ-C-320B (Bright finish) Class 1, Type I

23

Chromium SatinCHROMIUM PLATING – QQ-C-320B (Satin Finish) Class 1, Type II

24

Chromium EngineeringCHROMIUM PLATING QQ-C-320-B (Engineering), Class 2

25

Clear LacquerCLEAR LACQUER

26

Water Dip LacquerWATER DIP LACQUER

27a

Zinc Plate Type IZINC PLATE – ASTM B633/85 Type I – Class FE/ZN5-SC-1 (thickness .00025)
27bZinc Plate Type IIZINC PLATE – Colored Chromate – ASTM B633/85 Type II – FE/ZN5- SC-1 (thickness -.00025)
27cZinc Plate Clear
27dZinc Plate PhosphateZINC PLATE – (Phosphate Coat) -ASTM B633/85 Type V Class FE/ZN5-SC-1 (thickness .00025)
27eZinc Plate OliveZINC PLATE – per QQ-Z-325 Type II, olive drab.

28

Solder Plate.0001 to -.0003 Thick. Solder per QQS-571-F, SN 60 PG 40 over Nickel Plate thickness 0.0001-0.0005. In AC/W MILP-81728A plus solderability

29

Black Chrome Satin

30

Black Phosphate

31

Black Zinc

32

Black FinishUsed on steel parts – strictly cosmetic
33Electro-Tin PlateOver COPPER FLASH – MIL T – 10727C Type I

34a

Lubricant, Type ISolid Film – Heat cured – corrosion inhibiting – MIL-L-460101-AMEND #2, Type I, cure temperature of 150 ±3 º C.
34bLubricant, Type IISolid Film – Heat cured – corrosion inhibiting – MIL-L-460101B-AMEND #2, Type II, cure temperature of 204 ±3 º C.
35Electro PolishNo military specification assigned – An electric process used to remove the outer layer of material to brighten primarily steel-stainless steel and brass alloys.